The work investigated the anisotropy of corrosion properties of extruded low-alloy magnesium alloy ZX10 in two orthogonal sections (longitudinal TD and transverse ED). Using the EBSD and SEM methods, it was established that the TD section is characterized by the dominance of grains with a basal orientation and a stringer-like distribution of second-phase particles (relative area ~0.1%) oriented along the extrusion direction. In the ED section, the prismatic-pyramidal texture predominates, the particles are distributed more evenly, and their relative area is smaller than in the longitudinal section (~0.065%). Corrosion tests in 0.9% NaCl at 37°C for 168 h showed that the integral corrosion rates (determined by mass and volume loss) for both sections are similar, despite the different texture. However, detailed quantitative analysis of damage morphology using confocal laser scanning microscopy (CLSM) revealed significant differences in the nature of pitting corrosion. In the TD section, a larger relative area of pits was observed (14% versus 6% in ED), but their average depth was smaller (90 versus 186 µm) and their axial growth rate was two times lower. It has been shown that the initiation and growth of pits correlate with the location of second-phase particles. It is suggested that the slight differences in the integral corrosion rate of the two sections of the extruded rod are likely explained by the opposite influence of two factors: a favorable basal texture but a high density of string-distributed particles in the TD section and, conversely, an unfavorable texture but a uniform distribution of particles in the ED section. The paper demonstrates the effectiveness of CLSM for quantitatively separating the contribution of different types of corrosion.
Merson et al. (Sun,) studied this question.