To investigate the inevitable aging of composite insulators under the coupled effects of electrical, thermal, ice, and fog stresses, as well as to explore their aging mechanisms and residual strength prediction methods, this study collected operational insulator samples from four environmental regions: Tibet, Yunnan, Hunan Xuefeng Mountain, and Anhui/Chongqing. Mechanical properties, including tensile strength, elongation at break, and shear resistance, were tested. The results indicate that the degradation of mechanical performance in composite insulation components can be attributed to the synergistic interaction of operational environments and material characteristics, with the aging behavior of high-temperature vulcanized (HTV) silicone rubber exhibiting significant non-linearity. Based on existing research, molecular dynamics simulations were employed to construct microstructural models at different aging stages, and it was verified that main chain scission, reduced system density, and changes in the elemental chemical environment during aging are closely related to the degradation of material mechanical properties. Based on hyper-elastic constitutive theory and fracture mechanics, a quantitative method for assessing the comprehensive aging degree was proposed, with “service years” and “operational altitude” as the core dimensions. A negative exponential model was established to describe the strength degradation of silicone rubber materials. This model enables the non-destructive estimation of the residual mechanical strength of in-service insulators in complex regions without power interruption, providing a decision-making framework for grid operation and maintenance.
Zhang et al. (Wed,) studied this question.