To promote circular economy in construction, this study evaluates the mechanical surface integrity and long-term water durability of sustainable low-density particleboards utilizing agro-forestry residues, such as corn cob, corn stalk, hemp shive and wood fibres. These are bonded using an ecological mimosa tannin adhesive in comparison to a conventional urea–formaldehyde-based adhesive. Performance was assessed through apparent density, surface cohesion, Shore A hardness and impact resistance. Furthermore, the water sensitivity was assessed through total water absorption (WA), thickness swelling (TS), and a customized cyclic immersion-drying protocol. Results showed a significant correlation between density and Shore A hardness (R2 = 0.77). While hemp- and corn-based boards showed surface performance competitive with commercial standards, the wood fibre series exhibited extreme water susceptibility, with mass variations exceeding 400% during cycling. Additionally, tannin-based boards showed evidence of leaching, with an 11% mass loss after three emersion cycles. These findings conclude that while tannin adhesives are viable renewable alternatives, these bio-boards are primarily suited for interior lining in dry environments, as lightweight formulations require additional protection to ensure durability in practical building applications.
Paulino et al. (Sun,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: