Environmental concerns related to synthetic filler reinforced polymer composites have led to rapid advances in sustainable bio-based materials. The originality of this research is in crafting Margosa gum reinforced epoxy composites and determining the ideal filler loading for multi-functionality. The composites with effects from 0 to 25 vol% of Margosa gum were produced through vacuum-assisted casting and tested for their mechanical, thermo-mechanical, dielectric, and moisture resistance properties. The hydroxyl-rich functional groups which facilitate strong interfacial bonding between filler and matrix were identified by FTIR analysis. Tensile strength rose from 32.5 MPa for neat epoxy to 45.6 MPa at a filler loading of 15 vol%, whereas flexural strength was increased from 72.4 MPa to 97.8 MPa. The highest impact strength (5.8 kJ/m 2 ), storage modulus (3.02 GPa), and dielectric strength (33.5 kV/mm) corresponded to the MG–20 composite. At 15 vol% filler loading, the water absorption dropped a lot to 17.8% from 31.4%. Increasing filler content led to an improvement in thermo-mechanical stiffness and thermal stability. Still, an overfilled situation (25 vol%) caused filler agglomeration and microvoid formation, thereby lowering the performance. Overall, MG–15 and MG–20 composites show the best-balanced multifunctional features suitable for lightweight structural and electrical insulation uses.
Venkatesan et al. (Wed,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: