Lunar regolith simulant (LRS) geopolymers are promising construction materials for lunar in situ resource utilization, but their brittle behavior and limited crack resistance restrict their structural applications. This study investigated the effect of basalt fiber length on the mechanical properties, failure modes, stress–strain behavior, constitutive relationship, and microstructure of CQU-1 LRS geopolymers. Basalt fiber-reinforced LRS geopolymers were prepared under weak alkali activation and high-temperature curing at 80 °C. The basalt fiber content was fixed at 0.1%, and six fiber lengths of 0, 6, 9, 12, 15, and 18 mm were considered. Compressive and flexural tests were conducted after curing for 1 d and 7 d, and the normalized stress–strain curves were fitted using the Saenz L.P., Carreira D.J., and Zhenhai Guo models. The results showed that basalt fiber length significantly affected the mechanical performance of LRS geopolymers. An appropriate fiber length improved strength, stiffness, ductility, and post-peak load-bearing capacity, whereas excessively short or long fibers weakened the reinforcing effect. The 15 mm fiber group exhibited the best overall performance. After curing for 1 d, its compressive strength reached 2.23 MPa, 49.7% higher than that of the control group, and its elastic modulus increased approximately 2.5-fold. After curing for 7 d, its compressive strength reached 13.44 MPa, 32.0% higher than that of the control group. The Zhenhai Guo model provided the best fit for the stress–strain curves. SEM-EDS analysis showed that basalt fibers improved interfacial bonding and promoted gel enrichment near the fiber–matrix interface. Overall, 15 mm was recommended as the optimal basalt fiber length for CQU-1 LRS geopolymers under the conditions used in this study.
Zhan et al. (Tue,) studied this question.