Sensing based on Nitrogen-Vacancy (NV) centers in nanodiamonds (NDs) offers significant potential across various applications. However, optimizing their quantum-optical properties remains challenging. This study focuses on enhancing and controlling the optical properties of NV centers in NDs through surface chemistry tuning and proton beam irradiation. Systematic thermal oxidations were performed to investigate the evolution of surface chemical groups using IR spectroscopy and their influence on optical properties using photoluminescence spectroscopy and PL decay measurements. Proton irradiation was explored over a wide range of fluences (10¹4 to 10¹7 cm^-2) to precisely control the NV center concentration, identifying conditions that maximize creation and emission intensity. Furthermore, NV center charge state control was achieved by analyzing the NV-/NV0 ratio with varying surface terminations and NV center concentrations. A novel predictive mathematical model was developed to evaluate the efficiencies of forming NV- and NV0. Although tested specifically with proton-irradiated NDs, this model has broad applicability, representing a significant advancement in predicting the outcomes of ion-beam-based color center generation in diamond.
Aprà et al. (Mon,) studied this question.