Chloride-induced deterioration is a major threat to the durability of marine concrete structures, especially in tidal and submerged zones. This study simulated these environments by immersing C45 concrete specimens in NaCl solutions (5%, 10%, 15%) under both constant immersion and wet–dry cycles. Compressive strength tests, low-field NMR for pore structure, chloride ion profiling, and SEM-EDS analyses were conducted. A modified chloride diffusion model was developed based on Fick’s second law, incorporating time- and concentration-dependent parameters. The results showed that higher NaCl concentrations and tidal zone exposure significantly accelerated concrete degradation. In the tidal zone, wet–dry cycles led to larger macropore formation, higher chloride penetration, and more severe microstructural damage compared to the submerged zone. Compressive strength initially increased and then declined in high-salinity environments, with strength losses reaching up to 25% under 15% NaCl after 120 days. NMR data confirmed the transformation of micropores and mesopores into macropores, especially in the tidal zone. SEM-EDS analysis revealed decalcification, gypsum formation, and Friedel’s salt accumulation on eroded surfaces. It was determined that chloride ion diffusion behavior in concrete is significantly influenced by the chloride content and diffusion concentration, as well as the exposure zone. The developed model indicates that depth increased over time and with concentration. The proposed diffusion model achieved high fitting accuracy (R2 > 0.97), effectively capturing the effects of erosion age and salt; this makes it a reliable tool for predicting chloride ion ingress in marine concrete, and for supporting service life evaluation and durability design.
Luo et al. (Sat,) studied this question.