The long-term stability of rock–concrete composites largely depends on the mechanical properties and durability of the rock–concrete interface. This study investigated the coupling effect of interfacial roughness and acid sulfate corrosion on sandstone–concrete composites by using uniaxial compression tests combined with acoustic emission (AE) monitoring. The results showed that corrosion continuously reduces the mechanical properties of the specimens with peak strength and elastic modulus, exhibiting a two-stage evolution: rapid degradation in the early stage followed by a slow decline in the later stage. After 60 days of corrosion, the peak strength for composites with JRC = 5, JRC = 10, and JRC = 15 interfaces decreased by 46.59%, 44.34%, and 50.43%, respectively. The elastic modulus exhibited the same pattern of variation, and the decreasing rate was 68.90%, 66.96%, and 76.46% for the JRC = 5, JRC = 10, and JRC = 15 groups. Acoustic emission activities appeared earlier and were more significant after corrosion. With the effect of corrosion, the fracture mode evolved from tensile-dominated cracks to mixed tensile–shear cracks with a stronger shear component. Fractal analysis of AE energy revealed that the Hurst exponent decreased from 0.842–0.864 in the natural state to 0.503–0.567 after 60 days of immersion, whereas the fractal dimension increased from 1.136–1.182 to 1.433–1.497, indicating a decrease in the persistence and increase in complexity of the acoustic emission energy release process. Overall, the moderately rough interface (JRC = 10) achieved a better balance between initial strengthening and long-term corrosion resistance. These findings provide experimental support for evaluating the durability of sandstone–concrete composites in acidic sulfate environments.
Zhang et al. (Fri,) studied this question.