The durability of carbon black supported Pt and multiwalled carbon nanotubes supported Pt (Pt/CNTs) catalysts for potential application in polymer electrolyte membrane fuel cells are investigated using an accelerated durability test. The electrochemical surface area of degrades by 49.8% during the test time, compared with 26.1% for Pt/CNTs, which is due to Pt particle growth and Pt loss from the support in the form of Pt ions and Pt particles. Transmission electron microscopy and X-ray diffraction analysis show that Pt particles in present higher sintering resistance. X-ray photoelectron spectroscopy characterization indicates that CNTs in are more resistant to electrochemical oxidation than carbon black in . It can be concluded that are more stable under electrochemical operation, which can be attributed to specific interaction between Pt and the support and the higher resistance of the support to electrochemical oxidation.
Shao et al. (Sun,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: