The Dependence of Solid Electrolyte Interphase on the Crystal Facet of Current Collector in Li Metal Battery

The continuous electrolyte decomposition and uncontrolled dendrite growth caused by the unstable solid electrolyte interphase (SEI) have largely hindered the development of Li metal batteries. Here, we demonstrate that tuning the facet of current collector can regulate the composition of SEI and the subsequent Li deposition behavior using single-crystal Cu foils as an ideal platform. The theoretical and experimental studies reveal that the (100) facet of Cu possesses strong adsorption to anions, guiding more anions to participate preferentially in the inner Helmholtz plane and further promoting the formation of the stable inorganic-rich SEI. Consequently, the single-crystal Cu foils with a single 100 orientation (s-Cu(100)) achieve the dendrite-free Li deposition with enhanced Li plating/stripping reversibility. Moreover, the Li anode deposited on s-Cu(100) can stabilize the operation of an Ah-level pouch cell (350 Wh kg