The mechanical, thermal, physicochemical and structural properties of a thermoplastic cassava starch obtained by a twin-screw extrusion process were evaluated, using glycerol and isosorbide as plasticizers at different concentrations (30, 35 and 40% by weight) and storage times (1, 15 and 30 days) under controlled conditions of relative humidity of 47 ± 2% and temperature of 25 ± 2 °C. The results obtained show a decrease in tensile strength and modulus of elasticity and an increase in elongation in the initial measurements, suggesting that, in both cases, a plasticization phenomenon via absorption of humidity predominated in short times, while at prolonged times, a rigidification of the material occurred due to the generation of a retrogradation process. Likewise, a higher tensile strength and lower elongation were found in the materials plasticized with isosorbide. Finally, it was observed that the retrogradation phenomenon was more evident in the thermoplastic starch samples made with glycerol, and that the starches plasticized with isosorbide had lower moisture absorption, higher crystallinity and a predominantly Eh-type crystalline pattern, related to greater stability over time.
Acosta-Tirado et al. (2025) studied this question.