As the work hardening rate increases during the cold drawing of non-heat-treated steel (NHT steel), a significant loss in ductility and toughness can occur, leading to reduced formability and part quality. In this study, a bidirectional drawing process consisting of alternating forward and reverse passes is proposed to mitigate these issues and enhance the mechanical performance of the steel. Mechanical property evaluations, including tensile testing and three-point bending tests, were conducted to assess the effects of bidirectional drawing compared to conventional unidirectional drawing. The results showed that the bidirectionally drawn wire maintained a similar tensile strength to that of the unidirectionally drawn wire at a 70% area reduction, while exhibiting a 12% improvement in elongation. Microstructural analysis revealed grain refinement and reduced texture anisotropy in the bidirectionally drawn specimens, contributing to the observed enhancement in ductility. These findings indicate that bidirectional drawing is a promising approach for improving the formability and overall quality of high-strength, NHT steel components.
Lim et al. (2026) studied this question.