The presence of antibiotics in aquatic systems presents significant ecological and health risks. Herein, Fe3O4/MgAl2O4 (MgFeAl-1), 2.5%NiO@Fe3O4/MgAl2O4 (MgFeAl-2), 5%NiO@Fe3O4/MgAl2O4 (MgFeAl-3), and 10%NiO@Fe3O4/MgAl2O4 (MgFeAl-4) were synthesized, selecting glucose as a capping agent, and 600 °C as calcination temperature. The TEM, EDX, BET, XRD, and FTIR techniques were employed to characterize the preidentified sorbents. The average size of MgFeAl-1, MgFeAl-2, MgFeAl-3, and MgFeAl-4 was about 6.53, 5.0, 7.61, and 10.52 nm, respectively, and they exhibited surface areas of 114.15, 154.02, 153.36, and 128.54 m2 g−1, respectively. The sorbents were tested for the removal of ciprofloxacin (CFCN) from aqueous solutions using the batch protocol. The MgFeAl-2 exhibited the highest performance, achieving an adsorption capacity of 99.45 mg g−1, and the sorption equilibrium was reached within 60 min. The pseudo-second-order model best described CFCN sorption onto MgFeAl-2, and liquid-film diffusion influenced CFCN sorption. The CFCN adsorption onto MgFeAl-2 was well represented by the Langmuir isotherm model (R2 = 0.93), indicating a monolayer adsorption. The thermodynamic results indicated a spontaneous, endothermic sorption process. A four-cycle MgFeAl-2 reusability study showed an average efficiency of 90%. Notably, MgFeAl-2 was effective in treating natural-water matrices, with a slight reduction in seawater due to ionic interference. The findings highlight the potential of MgFeAl-2 as an affordable and reusable adsorbent for removing antibiotics from contaminated water.
Soad S. Alzahrani (2026) studied this question.