Effect of oxygen on fatigue crack growth in P92 steel at 600 °C: Atmosphere and vacuum
KW
K. Wang
East China University of Science and Technology
XB
X.F. Bai
Northwest Institute For Non-Ferrous Metal Research
ND
Nai-Jian Dong
East China University of Science and Technology
See all
Key Points
Fatigue crack growth increased significantly in P92 steel exposed to oxygen.
The study observed a 60% increase in crack growth rate when compared to vacuum conditions.
Analysis of fatigue crack growth under varying oxygen levels at 600 °C revealed important insights into material performance.
Enhancing understanding of oxygen's role may help improve the longevity of P92 steel components in industrial applications.
Mark Helpful
Like
Save
Bookmark
Relay
Share
Mark Helpful
Like
Save
Bookmark
Relay
Share
Effect of oxygen on fatigue crack growth in P92 steel at 600 °C: Atmosphere and vacuum | Synapse
Cite This Study
Copy
Wang et al. (Fri,) studied this question.
synapsesocial.com/papers/69a75e92c6e9836116a294ec
https://doi.org/https://doi.org/10.1016/j.corsci.2026.113680