Composite materials of porous pyrolyzed polyacrylonitrile-sulfur@graphene nanosheet (pPAN-S@GNS) are fabricated through a bottom-up strategy. Microspherical particles are formed by spray drying of a mixed aqueous colloid of PAN nanoparticles and graphene nanosheets, followed by a simple heat treatment with elemental sulfur. The pPAN-S primary nanoparticles are wrapped homogeneously and loosely within a three-dimensional network of graphene nanosheets (GNS). The hierarchical pPAN-S@GNS composite shows a high reversible capacity of 1449.3 mAh g(-1) sulfur or 681.2 mAh g(-1) composite in the second cycle; after 300 cycles at a 0.2 C charge/discharge rate the capacity retention is 88.8 % of its initial reversible value. Additionally, the coulombic efficiency (CE) during cycling is near 100 %, apart from in the first cycle, in which CE is 81.1 %. A remarkable capacity of near 700 mAh g(-1) sulfur is obtained, even at a high discharge rate of 10 C. The superior performance of pPAN-S@GNS is ascribed to the spherical secondary GNS structure that creates an electronically conductive 3D framework and also reinforces structural stability.
Wang et al. (2013) studied this question.