Abstract This paper investigates the precipitation microstructures in aluminium alloys 7040 and 7050 (Al - Zn - Mg - Cu variants) as a function of quench rate and aging treatment, and the associated compromise between yield strength and fracture toughness. The precipitate microstructures are quantitatively characterised by a combination of techniques covering the different scales involved: transmission electron microscopy (TEM), field emission gun scanning electron microscopy (FEG-SEM) and small angle X-ray scattering (SAXS), and fracture toughness is estimated using the Kahn tear test. Yield strength and strain hardening behaviour are determined by conventional tensile tests. It is shown that the composition modification from alloy 7040 to alloy 7050 results in a better compromise between yield strength and toughness. The strength decrease in alloy 7040 following a slow quench is much reduced compared to alloy 7050 because of a lower sensitivity to quench-induced precipitation on dispersoids. Both alloys...
Dumont et al. (2004) studied this question.