Synthesis of the Orthorhombic Phase of 2Y˙ZrO 2

A mixture of tetragonal and monoclinic 2Y˙ZrO 2 (2 mol% Y 2 O 3 –ZrO 2 ) powder was treated from 400° to 800°C and from 4 to 7 GPa for 30 min. The products were identified by powder XRD, Raman spectroscopy, and TEM. Results indicated that an orthorhombic phase was synthesized at T=400° to 600°C and P>4 GPa. The lattice parameters were obtained as a=0.505, b=0.525, and c=0.509 nm; the density was 6.17 Mg/m 3 . The orthorhombic phase always coexisted with the tetragonal phase in the products. The amounts of the tetragonal phase before and after treatment remained largely unchanged, whereas the amount of new orthorhombic phase was nearly the same as the decreased amount of the monoclinic phase. It was assumed, therefore, that only the monoclinic phase transformed into the orthorhombic phase.