Wood-based activated carbon was modified by impregnation with urea and heat treatment at 450 and 950 °C. The chemical and physical properties of materials were determined using acid/base titration, FTIR, thermal analysis, IGC, and sorption of nitrogen. The surface features were compared to those of a commercial urea-modified carbon. Then, the H 2 S breakthrough capacity tests were carried out, and the sorption capacity was evaluated. The results showed that urea-modified sorbents have a capacity similar to that of the received material; however, the conversion of hydrogen sulfide to a water-soluble species is significantly higher. It happens due to a high dispersion of basic nitrogen compounds in the small pores of carbons, where oxidation of hydrogen sulfide ions to sulfur radicals followed by the creation of sulfur oxides and sulfuric acid occurs. It is proposed that the process proceeds gradually, from small pores to larger, and that the degree of microporosity is an important factor.
Adib et al. (1999) studied this question.