The double perovskite oxide PrBaFe2O5+δ has great potential as a cathode material for solid oxide fuel cells (SOFCs). However, the electrochemical characteristics of Fe-based double perovskites are relatively inferior. To improve its electrochemical performance, Ca is investigated to partially replace Pr, forming Pr1–xCaxBaFe2O5+δ (PCBFx, x = 0.0–0.3) by an electrospinning technique. The PCBFx nanofibers exhibited a crystalline structure characterized by orthorhombic symmetry and space group P4/mmm. Furthermore, these PCBFx nanofibers displayed exceptional chemical compatibility with the Sm0.2Ce0.8O1.95 (SDC) electrolyte when sintered at a temperature of 900 °C for 5 h. The X-ray photoelectron spectroscopy (XPS) analysis reveals a progressive increase in the Fe4+ concentration as the Ca doping level rises. The polarization resistances (Rp) of the PCBF00, PCBF01, PCBF02, and PCBF03 nanofiber cathodes were 0.103, 0.079, 0.056, and 0.048 Ω cm2 at 750 °C. In the meantime, doping Ca increases the peak power density of the single cell by 46%, from 762.80 (PCBF00) to 1114.85 (PCBF03) mW cm–2 at 750 °C. The results demonstrate that PCBF03 double perovskite nanofibers exhibit great potential as cathode materials for SOFCs.
Fu et al. (Mon,) studied this question.