This paper focuses on high-entropy spinels, which represent a rapidly growing group of materials with physicochemical properties that make them suitable for hydrogen energy applications. The influence of high-pressure pure hydrogen on the chemical stability of three high-entropy oxide (HEO) sinter samples with a spinel structure was investigated. Multicomponent HEO samples were obtained via mechanochemical synthesis (MS) combined with high-temperature thermal treatment. Performing the free sintering procedure on powders after MS at 1000 °C for 3 h in air enabled achieving single-phase (Cr0.2Fe0.2Mg0.2Mn0.2Ni0.2)3O4 and (Cu0.2Fe0.2Mg0.2Ni0.2Ti0.2)3O4 powders with a spinel structure, and in the case of (Cu0.2Fe0.2Mg0.2Ti0.2Zn0.2)3O4, a spinel phase in the amount of 95 wt.% was achieved. A decrease in spinel phase crystallite size and an increase in lattice strains were established in the synthesized spinel powders. The hydrogenation of the synthesized samples in a high-pressure hydrogen atmosphere was investigated using Sievert’s technique. The results of XRD, SEM, and EDS investigations clearly showed that pure hydrogen at temperatures of up to 250 °C and a pressure of up to 40 bar did not significantly impact the structure and microstructure of the (Cr0.2Fe0.2Mg0.2Mn0.2Ni0.2)3O4 ceramic, which demonstrates its potential for application in hydrogen technologies.
Domaradzki et al. (Thu,) studied this question.