In order to improve the corrosion resistance of Mg-3Gd-1Zn-0.4Zr (GZ31K) alloys for biomedical application, the alloy was micro-arc oxidation (MAO)-treated using silicate electrolyte system under various voltages (400 V, 425 V, 450 V, 475 V). The effects of voltage on the microstructure and corrosion properties of MAO coating were investigated via X-ray diffraction (XRD) and a scanning electron microscope (SEM) combined with an energy-dispersive spectrometer (EDS), X-ray photoelectron spectroscope (XPS), and electrochemical experiments. The results showed that, with the increase in voltage, the MAO coatings became thicker and the micropores on the MAO coating increased in diameter. The main phase compositions of the MAO coatings were MgO and Mg2SiO4. Potentiodynamic polarization curve results showed that MAO coatings could enhance corrosion resistances, where the corrosion current density decreased by six orders of magnitude and the corrosion potential of the specimens increased by 300 mV for the voltage of 450 V in the MAO treatment; nevertheless, the corrosion resistance rapidly deteriorated due to the creation of large micropores in the MAO coating, which provide a pathway for corrosive media when the voltage is 475 V. The electrochemical impedance spectroscopy results showed that MAO treatments could increase low-frequency modulus resistance and increase the corrosion resistance of Mg alloys. In addition, MAO-treated GZ31K alloys still exhibited uniform corrosion, which is desirable for biomedical applications.
Geng et al. (Thu,) studied this question.