The objective of this in vitro study was to investigate the effects of dentin pretreatment protocols and thermocycling on the shear bond strength (SBS) of a self-adhesive resin cement (Maxcem elite chroma) on dentin. A total of 168 extracted human third molars were randomly divided into four main groups according to dentin pretreatment: no treatment, 10% polyacrylic acid, Optibond universal, and Scotchbond universal plus. Half of these were subjected to thermocycling (5000 cycles; 5–55 °C). Composite resin rods were bonded using the self-adhesive resin cement, and SBS was measured with a universal testing machine. Two-way ANOVA showed that dentin pretreatment and thermocycling significantly affected SBS, with significant interaction between factors (p < 0.001). The highest SBS was observed in the Optibond universal group (18.71 ± 0.43 MPa), while the lowest SBS occurred in the 10% polyacrylic acid-treated group after thermocycling (2.69 ± 0.39 MPa). Thermocycling significantly reduced SBS in all groups. These results indicate that pretreatment with a compatible universal adhesive improves bond durability, whereas 10% polyacrylic acid pretreatment adversely affects bonding performance.
Thatphet et al. (Tue,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: