In low Earth orbit (LEO), special environments such as atomic oxygen (AO), alternating high and low temperatures, and high vacuum can seriously affect the reliability and service lifetime of moving parts of space equipment. Therefore, there is an increasingly urgent demand for long-life, high-performance lubricating protective coatings with the rapid evolution of astronautical technology. In this study, polyimide (PI) was modified by polyhedral oligomeric silsesquioxane (POSS) with different numbers of functional groups to fabricate PI-based self-stratifying gradient composite lubricating coatings. The coating exhibited significantly enhanced AO resistance, and its vacuum tribological properties under alternating high and low temperature conditions were investigated. Results show that the mass loss of the gradient coating under AO exposure was significantly reduced by 78%, and the tribological properties of the coating under high and low temperature alternating conditions were significantly different. The friction coefficient was more stable and was smaller than that at high temperatures, and the wear rates of the POSS-modified coating also decreased by 77.5% and 50% for both high and low temperatures compared with that of the PI/PTFE coating.
Yu et al. (Fri,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: