Medium-entropy alloys (MEAs) with a simple phase structure and nanoprecipitates have excellent mechanical properties and considerable potential for advanced structural applications. The current study investigated the effect of boron microalloying and thermomechanical treatment on the microstructure evolution and mechanical properties of Co43Cr15Ni30Al5Ti7 and (Co43Cr15Ni30Al5Ti7)99.7B0.3 MEAs. X-ray diffraction analysis revealed a single phase of face-centered cubic (FCC) structure in all as-cast samples. After cold rolling and recrystallization annealing were completed, a clear ordered FCC (L12) phase was observed concurrently with the FCC matrix. In the alloy doped with 0.3 at.% B, the grain size was refined from 600 to 200 nm. TEM analysis revealed a nano-sized L12 phase coherently embedded in the FCC matrix. Analysis of the mechanical properties of boron-doped MEA samples revealed that cold rolling to 80% thickness followed by annealing at 900 °C for 2 h and aging at 750 °C for 4 h yielded the best mechanical performance. Among all samples, the alloy doped with 0.3 at.% boron achieved an optimal combination of mechanical properties (yield strength: 1817 MPa; ultimate tensile strength: 2313 MPa; ductility: 14.5%).
Chen et al. (Thu,) studied this question.