The main aim of this study was to evaluate the applicability of a low-cost, double-wall gas metal arc welding (GMAW)-based wire arc additive manufacturing (WAAM) process for aluminum alloy AlMg5, with an emphasis on microstructural heterogeneity, layer-dependent defect formation, and their implications for mechanical performance and geometric characteristics. A Taguchi L9 (33) design of experiments was employed to investigate the influence of welding current (40–60 A), shielding gas flow (10–20 L/min), and arc correction (0–40%) on wall geometry, material utilization, and overall process quality through multi-response optimization. The optimal parameter set (60 A, 15 L/min, 0% arc correction) resulted in a 54.9% improvement in the Grey Relational Grade compared to the lowest-performing configuration. Metallographic analysis revealed heterogeneous grain evolution governed by the multilayer thermal history, with porosity levels ranging from 3.20% to 3.49% and lack-of-fusion defects preferentially concentrated in interlayer and mid-height regions. The fabricated high-wall structure exhibited hardness values between 72 and 85 HV and an average ultimate tensile strength of 175 MPa. The observed mechanical scatter was consistent with localized microstructural heterogeneity and spatial defect distribution. The results demonstrate that geometric evaluation alone is insufficient as a quality metric for WAAM components and must be complemented by metallographic integrity assessment. Overall, the study highlights the importance of direct parameter optimization in double-wall WAAM structures to mitigate defect formation and enhance mechanical reliability under industrially accessible deposition conditions.
Krolo et al. (Thu,) studied this question.