Wire-arc coatings have received substantial attention for corrosion protection; however, poor bonding often leads to delamination, corrosion initiation, and costly re-coating of structural components. This review combines bibliometric mapping with a focused technical synthesis to clarify how bonding performance has been studied in wire-arc coatings. Specifically, publication trends, keyword co-occurrence networks, and country-level co-authorship maps are used to map the evolution of the field and position adhesion-related studies within the broader literature. The analysis of 762 wire-arc coating publications from Web of Science (among 13,314 thermal spray coating records) reveals that research is centered on microstructure, mechanical properties, and corrosion resistance, with growing links to wire-based additive manufacturing. Keyword co-occurrence networks demonstrate clear process–structure–property relationships, while country-level collaboration maps highlight the leadership of China, the USA, and Germany. Critical to note, only eight publications systematically investigate the combined effects of substrate roughness, coating thickness, and Zn-Al coating composition on bond strength—representing less than 0.01% of the thermal spray literature. This pronounced research gap underscores the novelty of the present review, which synthesizes existing knowledge on adhesion mechanisms, identifies key process parameters, and establishes a research agenda to optimize wire-arc coatings for infrastructure corrosion protection. The technical synthesis highlights that adhesion is governed by the coupled effects of surface preparation (roughness and topography), coating build-up (thickness), and spray conditions (e.g., standoff distance and substrate preheating), which together influence coating microstructure and failure modes. These findings provide a structured framework to guide parameter selection for durable coatings.
Badin et al. (Fri,) studied this question.