To elucidate the degradation behavior of elastic modulus in normal-strength ordinary concrete under flexural fatigue loading, this study systematically examines its evolution in C50 concrete, which is widely used in engineering applications. Based on four-point bending fatigue test data of plain concrete (PC) and reinforced concrete (RC) beams, degradation curves of the relative residual elastic modulus as a function of the cycle ratio were established. To quantitatively characterize the fatigue degradation process, two integrated indicators—the area under the curve (AUC) and the stable-stage degradation slope (|Kmid|)—were introduced to represent the degree of cumulative damage and the degradation rate of elastic modulus, respectively. These indicators were subsequently employed to evaluate the effects of maximum stress level, stress ratio, and reinforcement on elastic modulus degradation. The results show that failed PC specimens exhibited a typical three-stage S-shaped degradation pattern, whereas RC specimens primarily exhibited a two-stage degradation behavior. However, the elastic modulus of runout PC specimens remained above 93% of its initial value throughout the entire loading process. For PC specimens, under the same maximum stress level, increasing the minimum stress level from 0.10 to 0.25 resulted in a 24% decrease in |Kmid| from 0.2505 to 0.1912. At the same minimum stress level, increasing the maximum stress level from 0.75 to 0.90 led to a 94% increase in |Kmid| from 0.1912 to 0.3705. The presence of reinforcement increased AUC by 3~15% and reduced |Kmid| by 54~74%, indicating that reinforcement not only mitigated overall damage accumulation but also significantly slowed the degradation rate of the elastic modulus during the stable fatigue stage. The degradation characterization approach proposed in this study provides a simplified and practical framework for fatigue analysis of concrete components based on damage mechanics.
Chen et al. (Mon,) studied this question.