Regulating electrostatic phenomena by cationic polymer binder for scalable high-areal-capacity Li battery electrodes

Despite the enormous interest in high-areal-capacity Li battery electrodes, their structural instability and nonuniform charge transfer have plagued practical application. Herein, we present a cationic semi-interpenetrating polymer network (c-IPN) binder strategy, with a focus on the regulation of electrostatic phenomena in electrodes. Compared to conventional neutral linear binders, the c-IPN suppresses solvent-drying-induced crack evolution of electrodes and improves the dispersion state of electrode components owing to its surface charge-driven electrostatic repulsion and mechanical toughness. The c-IPN immobilizes anions of liquid electrolytes inside the electrodes via electrostatic attraction, thereby facilitating Li+ conduction and forming stable cathode-electrolyte interphases. Consequently, the c-IPN enables high-areal-capacity (up to 20 mAh cm-2) cathodes with decent cyclability (capacity retention after 100 cycles = 82%) using commercial slurry-cast electrode fabrication, while fully utilizing the theoretical specific capacity of LiNi0.8Co0.1Mn0.1O2. Further, coupling of the c-IPN cathodes with Li-metal anodes yields double-stacked pouch-type cells with high energy content at 25 °C (376 Wh kgcell-1/1043 Wh Lcell-1, estimated including packaging substances), demonstrating practical viability of the c-IPN binder for scalable high-areal-capacity electrodes.