The structure and thermoelectric (TE) properties of La-doped, A-site-deficient SrTiO3 (Sr1–3x/2LaxTiO3) ceramics sintered in air and N2/5% H2 have been investigated. Air-sintered ceramics with 0.10 ≤ x 0.50 are orthorhombic with an a–a–c+ tilt system and long-range VA ordering. x = 0.15 sintered in N2/5% H2 shows the largest dimensionless TE figure-of-merit ZT = 0.41 at 973 K reported for n-type SrTiO3-based ceramics, suggesting that the accommodation of La through formation of (VSr) coupled with reduction in N2/5% H2 represents a new protocol for the development of oxide-based thermoelectrics.