Multi-Objective Mix Design Framework for Solid-Waste-Based Self-Compacting Concrete

The growing demand for sustainable construction has highlighted the need to effectively utilize solid waste materials in concrete production, yet achieving satisfactory workability, strength, and durability simultaneously remains challenging. A multi-parameter mix-design methodology is proposed for solid-waste-based self-compacting concrete (SCC). This method couples minimum water demand, control of paste film thickness, and multi-performance balancing. The ternary solid-waste powder system (silica fume, fly ash, and supersulfated solid-waste-based cement) was first optimized through minimizing water demand to achieve maximum packing density. The resulting composition was then blended with varying dosages of ordinary Portland cement (OPC) to form the final cementitious binder. Aggregate gradation was proportioned to minimize voids, and paste volume was determined using an equivalent-paste-film-thickness model. Under comparable mixture conditions, SCC with OPC contents of 70–40 wt.% and paste film thicknesses of 2.0–2.6 mm was evaluated for fresh performance, compressive strength, freeze–thaw resistance, and material cost. Mixtures with a paste film thickness of 2.4 or 2.6 mm satisfied the self-compactability criterion—the mix with 50 wt.% OPC and a paste film thickness of 2.4 mm showed the best overall performance balance, achieving higher 28 d strength than higher-OPC mixtures while improving freeze–thaw resistance and reducing cost. Results from TGA, XRD, ATR–FTIR, and SEM–EDS analyses indicated enhanced calcium hydroxide (CH) consumption, increased formation of C-(A)-S-H and ettringite, and a denser interfacial transition zone (ITZ), supporting the proposed multi-objective design approach. While the framework was validated for a specific ternary binder system, it provides a reproducible proportioning strategy applicable to a broader range of solid-waste-based concrete systems, with potential for extension to other waste streams and exposure conditions, thus supporting the development of more resource-efficient and environmentally sustainable concrete.