Efficient joining of hard metals to steels is crucial for supporting sustainable manufacturing under emissions strategies to minimize CO2. CoNiCrFeCu high-entropy alloy containing scandium (Sc) was designed as a filler for laser braze-welding of WC-Co and steel. The designed compositions with different Sc levels were melted and cast in a high-vacuum non-consumable arc furnace. The results showed that the as-cast microstructure was a complex mixture of a networked Ni2Si, elongated Cr-Fe-Co solid-solution phase, and Fe-Ni-Co-Cu solid-solution phase. Scandium was shown to have formed compounds with nickel/cobalt and copper. The TG-DSC analysis confirmed that the melting points of the designed compositions were between 973.7 °C and 981.5 °C. The maximum spreading area of the CoNiCrFeCu-0.9Sc composition on AISI 1045 steel was 64.83 mm2, and on the WC-Co cermet it was 78.63 mm2. The interface between the fusion zone and AISI 1045 steel exhibited an epitaxial growth of dendrites from the steel base metal. The interface between WC-Co and the fusion zone exhibited a partial penetration of brazing filler into the Co matrix, forming a metallurgical bonding between the dissimilar materials. Sc, as an alloying element in the filler metal, enhanced the bond formation because it decreased the solidus temperature and increased wetting.
Xu et al. (Thu,) studied this question.