The AA8011 aluminium alloy is a lightweight structural and engineering alloy with relatively low mechanical strength, and localised corrosion weakens its performance in adverse environments. To overcome these limitations, ZrB-reinforced AA8011 aluminium matrix composites were fabricated using vacuum-assisted squeeze casting with varying reinforcement proportions (2 wt.%, 4 wt.%, and 6 wt.%) to exploit the synergistic effects of ceramic particle strengthening and microstructural modification. The inclusion of ZrB 2 helped refine the grains, disrupted the continuity of the Fe-rich intermetallic phases, and improved the interaction between the matrices and reinforcements, effectively transferring loads and strengthening the passive oxide layer. SEM observations reveal a finer and more uniform microstructure of the ZrB 2 -reinforced composites than the coarse dendritic microstructure of the base alloy. Although the elongation decreases from 26.84 ± 0.9% in the base alloy to 15.32 ± 0.6% in the 6 wt.% ZrB 2 composite, the material still retains reasonable ductility and exhibits significant increases in tensile (31.6%), compressive (37.14%), flexural (36.20%), and impact strengths (34.54%), as well as hardness (35.6%), all of which increase systematically with higher ZrB 2 content, and the corrosion rate is reduced to 37.72%. The results indicate that ZrB 2 reinforcement effectively addresses the inherent deficiencies of the AA8011 alloy, enabling the resulting composites to meet the stringent requirements of lightweight structural applications.
Ananth et al. (Fri,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: