Ceramic lead magnesium niobate–lead titanate ((1‐x)PMN ‐x PT) of different compositions has been prepared by the columbite precursor method. This study discusses compositions ranging from 0.94PMN–0.06PT to 0.60PM–N0.40PT, focusing on two areas of the (1‐x)PMN x PT system: compositions that exhibit electrostrictive behavior, and those that show piezoelectric behavior. In electrostrictive compositions where x is in the range of 0.06–0.20, the dielectric constant and electromechanical coupling factor dependencies on the bias field are evaluated. The optimal electromechanical properties are obtained with the composition 0.82PMN–0.18PT, measured at temperature T = T m (the temperature of maximum dielectric constant) = 80°C and with a dc bias of 5 kV/cm. X–ray diffractometry is used to show that the (1‐x)PMN ‐x PT system has a compositionally wide two–phase region and that 0.655PMN–0.345PT is the morphotropic phase boundary (MPB) composition. Electromechanical property evaluation shows that the optimal piezoelectric properties (piezoelectric charge coefficient ( d 33 ) value of 720 pC/N, dielectric constant ( K ) value of 5400, and electromechanical planar and thickness coupling coefficient ( k p and k t , respectively) values of 62% and 46%, respectively) are obtained at the MPB composition.
Kelly et al. (Tue,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: