Effect of polishing and glazing on the color and spectral distribution of monolithic zirconia

PURPOSE: The aim of this study was to evaluate the effect of polishing and glazing on the color and spectral distribution of monolithic zirconia. MATERIALS AND METHODS: Forty-five monolithic zirconia specimens (16.3 mm × 16.4 mm × 2.0 mm) were fabricated and divided into 5 groups according to the number of A2-coloring liquid applications (Group I to V). Each group was divided into 3 subgroups according to the method of surface treatments (n=3): N: no treatment; P: polishing; G: glazing. Color and spectral distribution of five different areas of each specimen were measured according to CIELAB color space in the reflectance mode relative to the standard illuminant D65 on a reflection spectrophotometer. Data were analyzed using one-way ANOVA followed by Tukey's HSD test, Pearson correlation and regression analysis (α=.05). RESULTS: There was a significant difference in CIE L (*) between Subgroup N and P, and in CIE b (*) between Subgroup P and G in each group. Spectral reflectance generally decreased in Subgroup P and G in comparison with Subgroup N. Color differences between Subgroup P and G were within the perceptibility threshold (ΔE (*) ab0.88, P<.001). CONCLUSION: A perceptible color difference can be detected after polishing of monolithic zirconia. Polishing decreases the lightness, and glazing also decreases the lightness, but increases the yellowness of monolithic zirconia.