Ultra-high-performance concrete (UHPC) is known for its exceptional compressive strength and durability; however, its brittle nature requires fiber reinforcement to improve toughness and tensile performance. This study investigates the synergistic effects of triple fiber reinforcement, including desized and sized carbon fibers (0.2–1.0 vol%), steel fibers (1.0 vol%), and polypropylene fibers (0.2 vol%) on the fresh, mechanical, durability, microstructure, and fire resistance properties of UHPC. The experimental program included workability, compressive and flexural strength, load-deflection behavior, electrical resistivity, dynamic modulus of elasticity, SEM analysis, and fire resistance at elevated temperatures (425 and 900 °C). The results showed that desized carbon fibers performed better than sized fibers by improving workability, fiber dispersion, flexural behavior, and fiber–matrix bonding. The optimal triple-fiber composition, DC1.0P0.2S1.0, achieved the highest flexural strength of 24 MPa while maintaining compressive strength above 141 MPa. The triple-fiber system provided effective multi-scale crack control, where PP fibers prevented explosive spalling, carbon fibers bridged meso-crack control, and steel fibers enhanced macro-crack load transfer and ductility. SEM analysis further confirmed better dispersion and stronger interfacial bonding of desized carbon fibers. Overall, the optimized triple-fiber system significantly improved flexural performance, toughness, workability, and fire resistance without notably reducing compressive strength, demonstrating strong potential for advanced structural applications.
Kumar et al. (Thu,) studied this question.