Introduction: This study aimed to assess and compare the efficacy of Nacre and casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) on the remineralization of enamel using surface microhardness analysis, scanning electron microscopy (SEM), and energy dispersive X-ray (EDX) spectroscopy. Materials and Methods: Twenty human maxillary premolars extracted for orthodontic reasons were collected. Under cool water spray, the crowns were sectioned mesiodistally into buccal and palatal halves using a diamond disc. The samples were subsequently mounted in self-cure acrylic resin. The samples were then subjected to Vickers hardness testing and SEM-EDX for baseline. To simulate carious lesions, all of the samples were acid-etched with 37% phosphoric acid for 30 s in a specific area on the enamel samples and subjected to surface microhardness testing and SEM-EDX. The enamel samples were randomly assigned to Group 1: Nacre water-soluble matrix (WSM), Group 2: Nacre varnish, and Group 3: CPP-ACP for remineralization. After 21 days, remineralization assessment of the test samples was done using SMH analysis and SEM-EDX analysis. Data obtained were statistically analyzed using the one-way analysis of variance to reveal the significant differences between the groups. Tukey’s test was used for post hoc comparisons. Results: All three groups showed a significant increase in surface microhardness. All three groups showed a significant calcium and phosphorous ratio increase after remineralization. Among the three groups, the highest Ca:P ratio was seen in the Nacre WSM group (0.58) followed by the Nacre Varnish (0.57) and CPP-ACP group (0.57). SEM images of the Nacre surface revealed the presence of extensive interlocking. A layer of packed hydroxyapatite particles was formed on the surface of the nacre through surface reactions. Conclusion: All the groups in the present study showed some extent of remineralizing ability irrespective of the different materials and mechanisms of action. Nacre WSM showed a remarkable hardness spike close to natural enamel after demineralization.
Reddy et al. (Sun,) studied this question.