Refill friction stir spot welding (refill FSSW) is a solid-state joining technique that enables dissimilar welding between aluminum and steel alloys with minimal intermetallic compound (IMC) formation. Previous studies have focused on the interfacial mechanical performance of such joints, limited attention has been given to the localized corrosion behavior of the aluminum surface after welding, particularly in relation to microstructural evolution. This study investigates the effect of refill FSSW on the localized corrosion resistance of the aluminum surface in dissimilar joints with DP600 steel, since the Al side is typically the exposed surface in automotive service conditions. Emphasis is placed on the correlation between microstructural changes induced by the welding thermal cycle, such as grain refinement and precipitate coarsening, and localized corrosion behavior. The welded samples were characterized by optical and scanning electron microscopy, Vickers hardness measurements and potentiodynamic polarization techniques. Corrosion tests revealed a slight reduction in corrosion resistance in the stir zone compared to the base metal, mainly attributed to Mg2Si coarsening. Pit initiation sites were associated with Al(Fe, Mn)Si and Mg2Si precipitates. These findings offer new insights into the corrosion mechanisms acting on the aluminum surface of refill FSSW joints, supporting the development of more corrosion-resistant dissimilar structures.
Carvalho et al. (Tue,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: