With the rapid depletion of natural graphite, the synthesis of artificial graphite from high-carbon precursors has garnered growing interest. However, conventional artificial graphitization typically requires extremely high temperatures. This study demonstrates that natural halloysite mineral can serve as an effective catalyst to lower the graphitization temperature threshold of anthracite. The results show that halloysite exerts a pronounced catalytic effect within the temperature range of 1400–2300 °C. The enhancement in graphitization is primarily attributed to the formation and subsequent decomposition of intermediate phases between halloysite and the carbon matrix. From 1400 to 1700 °C, the interlayer spacing decreases significantly with halloysite as a catalyst due to the nucleation of highly ordered “multilayer graphene” structures surrounding intermediates. However, these graphene layers exhibit a confined and curved morphology that spatially restricts crystallite growth, resulting in relatively small in-plane (La) and stacking (Lc) crystallite dimensions. Moreover, multilayer graphene originating from intermediate crystal corners tends to generate numerous dislocation defects. From 1700 to 2300 °C, significant increases in both La and Lc are observed, accompanied by a marked improvement in structural order. This evolution is driven by the progressive inward decomposition of intermediate phases, which causes the “circular-shaped” graphene domains to collapse at the dislocation defects and subsequent straightening of the curved graphene layers. These findings provide new microstructural insights into mineral-catalyzed graphitization mechanisms in anthracite and present a promising pathway toward energy-efficient production of synthetic graphite.
Zhang et al. (Thu,) studied this question.