Dislocation reduction in gallium nitride (GaN) epitaxial layers remains a critical challenge for high-performance GaN-based electronic devices. In this study, GaN epitaxial growth on newly-developed 4H-Silicon Carbide (SiC) meta-substrates was systematically investigated to elucidate the role of surface pattern geometry in modulating dislocation propagation. A series of truncated-hexagonal-pyramid meta-structures with a fixed array period and varying pattern ratios (R) were designed and fabricated to enable controlled tuning of the effective surface morphology. Atomic force microscopy confirmed comparable surface flatness for all samples after epitaxial growth. Cathodoluminescence analysis revealed a non-monotonic dependence of defect density on R, indicating the existence of an optimal pattern geometry. Among all configurations, the outstanding sample exhibited the lowest defect density, achieving a 54.96% reduction in threading dislocations (edge + mixed) compared with a planar reference. Cross-sectional transmission electron microscopy further confirmed a substantially reduced dislocation density and clear evidence of dislocation bending and termination near the meta-structured regions. These results demonstrate that geometry-engineered 4H-SiC meta-substrates provide an effective and scalable strategy for dislocation modulation in GaN epitaxy on SiC meta-substrates, offering a promising pathway toward advanced GaN power and RF devices.
Su et al. (Fri,) studied this question.