A novel low-cost poly(propylene carbonate-co-epichlorohydrin) (PPC-ECH) with mechanical properties similar to those of poly (butylene adipate-co-terephthalate) (PBAT) was developed and incorporated into a poly(propylene carbonate-co-phthalate) (PPC-P) matrix. Meanwhile, 4, 4’-diphenylmethane diisocyanate (MDI) was employed as a reactive compatibilizer and mixed with PPC-P and PPC-ECH to create a variety of PPC-P/PPC-ECH/MDI blends. The effects of PPC-ECH and MDI content on the mechanical, optical, thermal, morphological, and gas barrier properties of the blends were systematically investigated. Results demonstrated that MDI reacts with both PPC-P and PPC-ECH, forming a chemically bonded interface that significantly improves their compatibility. Notably, when 2 phr of MDI was incorporated, the elongation at break of the PPC-P/PPC-ECH/2MDI blend increased dramatically from 71% to 502%, while maintaining good tensile strength (~23 MPa) and light transmittance (~80%). To further enhance the gas barrier performance, a high-oxygen-barrier poly(vinyl alcohol) (PVA)/tannic acid (TA) complex coating was applied to the surface of the PPC-P/PPC-ECH/2MDI film. This coating synergistically leveraged the abundant hydroxyl groups in PVA and TA to form a dense hydrogen-bonded network, reducing oxygen permeability to an ultra-low value of 0.1 cm3·mm/(m2·day). This outstanding performance highlights the strong potential of PPC-P/PPC-ECH-based films for advanced packaging applications.
Yue et al. (Fri,) studied this question.