Effects of helium ion irradiation at high temperature on Inconel 617 with Ni cladding

Key Points

• Degradation occurs in Inconel 617 following helium ion irradiation, significantly affecting material integrity.
• Notable changes were observed in thermal properties after exposure to high temperatures and ion irradiation.
• Analysis across different exposure levels used helium ion irradiation to evaluate effects on nickel cladding stability.
• Findings highlight the importance of assessing long-term performance under high-temperature, space-related conditions.