Despite the rapidly increased power conversion efficiency (PCE) of perovskite solar cells (PVSCs), it is still quite challenging to bring such promising photovoltaic technology to commercialization. One of the challenges is the upscaling from small-sized lab devices to large-scale modules or panels for production. Currently, most of the efficient inverted PVSCs are fabricated on top of polybis(4-phenyl)(2, 4, 6-trimethylphenyl)amine (PTAA), which is a commonly used hole-transporting material, using spin-coating method to be incompatible with large-scale film deposition. Therefore, it is important to develop proper coating methods such as blade-coating or slot-die coating that can be compatible for producing large-area, high-quality perovskite thin films. It is found that due to the poor wettability of PTAA, the blade-coated perovskite films on PTAA surface are often inhomogeneous with large number of voids at the buried interface of the perovskite layer. To solve this problem, self-assembled monolayer (SAM)-based hole-extraction layer (HEL) with tunable headgroups on top of the SAM can be modified to provide better wettability and facilitate better interactions with the perovskite coated on top to passivate the interfacial defects. The more hydrophilic SAM surface can also facilitate the nucleation and growth of perovskite films fabricated by blade-coating methods, forming a compact and uniform buried interface. In addition, the SAM molecules can also be modified so their highest occupied molecular orbital (HOMO) levels can have a better energy alignment with the valence band maxima (VBM) of perovskite. Benefitted by the high-quality buried interface of perovskite on SAM-based substrate, the champion device shows a PCE of 18.47% and 14.64% for the devices with active areas of 0.105 cm2 and 1.008 cm2, respectively. In addition, the SAM-based device exhibits decent stability, which can maintain 90% of its initial efficiency after continuous operation for over 500 h at 40 ℃ in inert atmosphere. Moreover, the SAM-based perovskite mini-module exhibits a PCE of 14.13% with an aperture area of 18.0 cm2. This work demonstrates the great potential of using SAMs as efficient HELs for upscaling PVSCs and producing high-quality buried interface for large-area perovskite films.
Zeng et al. (Mon,) studied this question.