Wire electrical discharge machining (WEDM) is widely used for the precision cutting of difficult-to-machine materials, including nickel-based superalloys. Wire electrode wear, however, remains a practical limitation, because it affects process stability, wire consumption, and machining cost. This work examines the wear behaviour of a gamma-phase Cu5Zn8-coated copper-core wire electrode (Elecut X, ø 0.25 mm) during the WEDM of Inconel 718 using direct gravimetric measurement. A 33 full factorial experiment was carried out with three electrical parameters: pulse-on time (A), pulse-off time (B), and servo reference voltage (Aj). The discharge process was monitored with an oscilloscope so that measurements only started after the programmed pulse-off time had been reached. Electrode wear was evaluated as the mass loss Δm of 4 m wire segments after 5 min cutting intervals on a Charmilles Robofil 310 machine, and factor significance was assessed by analysis of variance (ANOVA). Pulse-on time was the dominant factor, accounting for 88.45% of the total variation in Δm, followed by servo reference voltage and pulse-off time. SEM/EDS examination showed material transfer from the Inconel 718 workpiece to the worn electrode surface, with local nickel content reaching 16.84 wt.% on the frontal face of the most worn sample. The results provide a quantitative basis for reducing wire consumption during the WEDM of Inconel 718 while recognising the trade-off with cutting productivity.
Šimna et al. (Sat,) studied this question.