Wire Arc Additive Manufacturing (WAAM) has emerged as a cost-effective and high-deposition-rate technique for fabricating large-scale metallic components; however, the complex thermal history inherent to the process leads to heterogeneous microstructures that can significantly influence tribological performance. In this study, the dry sliding wear behavior of WAAM-fabricated austenitic stainless steel 308L (SS308L) was systematically investigated using a pin-on-disk configuration. The influence of applied normal load (1.5–15 N) and sliding speed (0.03–0.229 m/s) on wear volume, specific wear rate, coefficient of friction (COF), and tangential force was evaluated. Optical microstructural observations indicated features consistent with a ferritic–austenitic solidification structure, including regions resembling polygonal ferrite, Widmanstätten ferrite, and austenitic dendritic morphologies. Wear results showed that wear volume and cross-sectional area increased monotonically with increasing load, while the effect of sliding speed was comparatively less significant. The specific wear rate remained on the order of 10−4 mm3/N·m with minor variations across test conditions. The COF decreased with increasing load up to 10 N, followed by a speed-dependent response at higher loads. The findings demonstrate that load is the dominant factor governing wear behavior in WAAM SS308L, while microstructural heterogeneity may contribute to frictional stability and wear resistance. This study provides valuable insight into the structure–tribology relationship of WAAM stainless steels and supports the optimization of process parameters for wear-critical applications.
Alzughaibi et al. (Sun,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: