Advanced thermal barrier coatings (TBCs) are essential for improving the efficiency and performance of gas turbine engines. Increasing engine operating temperatures and harsh service environments are pushing the current industry-standard 8 wt% yttria-stabilized zirconia (8YSZ) to its performance limits. High-rare-earth-oxide zirconates, such as Gd2Zr2O7, have emerged as promising materials for next-generation engines due to their excellent high-temperature phase stability, lower thermal conductivity, and enhanced resistance to CMAS attack. In this work, dense vertically cracked (DVC) Gd2Zr2O7/8YSZ bilayer coatings were developed using the air plasma spray (APS) process. Two approaches were employed for deposition of the NiCrAlYHfSi bond coat: (i) high-velocity oxygen fuel (HVOF), and (ii) APS flash-coated HVOF NiCrAlYHfSi bond coat. The durability of DVC TBC systems with the two bond coat types was evaluated by furnace cycling test (FCT) at 1125 °C. The TBC system with an APS flash-coated HVOF bond coat exhibited an FCT lifetime approximately twice that of the system with the HVOF bond coat alone. The improvement is primarily attributed to the higher surface roughness of the APS flash-coated bond coat, which enhances resistance to crack initiation, propagation, and linkage, thereby extending thermal cycling life.
Chen et al. (Tue,) studied this question.