Abstract We report a comprehensive study on influence of oxygen partial pressure on NiO thin films grown on glass substrates in a combined argon and oxygen ambience by reactive dc magnetron sputtering. In this present article, we have discussed the dependence of oxygen pressure on structural, chemical, morphological, optical and electrical properties of the sputtered NiO films. Glancing angle x-ray diffraction reveals that the deposited films were polycrystalline in nature with FCC phase. The preferred orientation changes from (200) to (111) in a higher O 2 flow rate environment and an average particle size was estimated using Scherrer relation. The surface morphology of films was studied by using atomic force microscopy. The x-ray photoelectron spectroscopy analysis demonstrates the core level Ni 2p spectra over a range of 850 eV to 885 eV of binding energy and observed Ni 2p 3/2 , Ni 2p 1/2 domains along with their satellite peaks. It infers the presence of both Ni +2 and Ni +3 oxidation states in the sputtered films. Additionally, Raman spectroscopy was carried out to confirm the structural defects level and crystalline nature of the films. The optical results show that deposited films were semi-transparent and the evaluated optical band gap of the material lies in the range 3.36 eV to 3.52 eV. The extracted electrical properties infer either n-type or p-type conductivity depending on the processing conditions of the films.
Salunkhe et al. (Wed,) studied this question.