Large-Scale Molecular Dynamics of Anion-Exchange Membranes: Molecular Structure of QPAF-4 and Water Transport

Understanding the molecular structure and water transport behavior in anion-exchange membranes (AEMs) is essential for advancing efficient and cost-effective alkaline fuel cells. In this study, large-scale all-atom molecular dynamics simulations of QPAF-4, a promising AEM material, were performed at multiple water uptakes (λ = 2, 3, 6, and 13). The simulated systems comprised approximately 1.4 to 2.1 million atoms and spanned approximately 26 nm, thus enabling direct comparison with both wide-angle X-ray scattering (WAXS) and small-angle X-ray scattering (SAXS) experiments. The simulations successfully reproduced experimentally observed structure factors, accurately capturing microphase-separated morphologies at the mesoscale (~8 nm). Decomposition of the SAXS profile into atom pairs suggests that increasing water uptake may facilitate the aggregation of fluorinated alkyl chains. Furthermore, the calculated pair distribution functions showed excellent agreement with WAXS data, suggesting that the atomistic details were accurately reproduced. The water dynamics exhibited strong dependence on hydration level: At low water uptake, mean squared displacement showed persistent subdiffusive behavior even at long timescales (~200 ns), whereas almost normal diffusion was observed when water uptake was high. These results suggest that water mobility may be significantly influenced by nanoconfinement and strong interactions exerted by polymer chains and counterions under dry conditions. These findings provide a basis for the rational design and optimization of high-performance membrane materials.