Analysis shows spatially heterogeneous degradation in LiFePO4 and graphite batteries, indicating temperature impacts failure mechanisms.
Temperature-accelerated aging behavior of LiFePO 4 //graphite batteries was investigated, highlighting spatial heterogeneity between inner and outer electrodes. The degradation disparity offers new insights into temperature-induced failure mechanisms.