Effects of Ultrasonic Vibration Intensity and Initial Powder Amount in the Hopper on Powder Dispensing Rate in Binder Jetting Additive Manufacturing

In binder jetting additive manufacturing (BJAM), parts are fabricated layer by layer by depositing a liquid binder on selected regions of the powder bed. Powder particles in the hopper of the printer are dispensed onto the powder bed to form a layer of powder. Powder dispensing rate affects material usage and print quality. Too high dispensing rates can cause excessive powder dispensing, increasing powder waste, while too low dispensing rates may result in incomplete layer formation, leading to reduced density of printed parts. The present study investigates how ultrasonic vibration intensity and initial powder amount in the hopper affect powder dispensing rate in BJAM when using a bimodal powder. A set of experiments with full factorial design were conducted using three levels of ultrasonic vibration intensity (50%, 75%, and 100%) and three levels of initial powder amount (600 g, 1000 g, and 1400 g) in the hopper. The results show that both ultrasonic vibration intensity and initial powder amount, as well as their interaction, significantly influence powder dispensing rate. Powder dispensing rate was higher when ultrasonic vibration intensity was higher or initial powder amount was smaller. Increasing initial powder amount from 600 to 1400 g, resulted in a much bigger decrease in powder dispensing rate when ultrasonic vibration intensity was 50% than when ultrasonic vibration intensity was 100%.