Microstructure and Compressive Properties of (Ti51Zr25Cu6Be18)100−xVx Bulk Metallic Glass Matrix Composites

Metallic glass alloys exhibit excellent properties, yet suffer from poor room-temperature plasticity, a limitation that restricts their engineering applications. Bulk metallic glass matrix composites (BMGMCs) have proven effective in enhancing the plasticity of metallic glasses, and the addition of alloying elements serves as a key strategy to regulate their microstructure and optimize the properties of these composites. This study aims to investigate the effects of a vanadium (V) addition on the mechanical properties and microstructure of Ti-based BMGMCs, while exploring the underlying mechanism of V’s influence. Using (Ti51Zr25Cu6Be18)100−xVx (x = 0, 4, 8, 12, 16, 20) BMGMCs as test specimens, microstructural characterization was performed via X-ray diffraction (XRD) and scanning electron microscopy (SEM), and compressive mechanical properties were tested. The results indicate that a V addition refines dendrites without altering the phase composition, which remains composed of β-Ti crystals and an amorphous matrix. With the increase in V content, the compressive plastic strain shows a trend of first increasing and then decreasing; when x = 12, the specimen exhibits the maximum compressive plastic strain, reaching 7.9%. Additionally, the volume fraction of the crystalline phase gradually increases with increasing V content. This study clarifies the mechanism by which V regulates the microstructure and properties of Ti-based BMGMCs, thereby providing theoretical and experimental insights for optimizing alloy compositions to enhance the mechanical performance.